Food Grade 30% Glass Fiber Reinforced PA66 Pellets

Name: Food Grade 30% Glass Fiber Reinforced PA66 Pellets
Brand: PRES
SKU: 548720907
Rating: 5.0 (61 reviews)

Food grade PA66 After hydrolysis-resistant reinforced , it is not prone to precipitation at high temperatures, has good color fastness, bright luster and is not easy to fade.

Material:	30% glass fiber reinforced PA66
Color:	nature black custom
MOQ:	1KG
Packing:	25kg/bag
Availability:

Quantity:



Inquire Add to Basket

Model:
PA66-FR30
Brand:
PRES

Product Description

PA66 GF30 Product Description

		High-temperature resistant
	1.Glass transition temperature: 90°C 2.Heat distortion temperature: 220-240°C 3.Long-term using temperature: 80-120°C 4.Short-term using temperature: 180°C
		Low shrinkage rate and low water absorption rate
	After glass fiber reinforced,Water absorption rate <1%,The shrinkage rate low to 0.3-0.6%. This makes it easier to control the tolerance of fiber-reinforced products during injection molding
		High strength
	The tensile strength of pure PA66 is 80-90 MPa, while PA66 with 30% fiber reinforced can reach 160-200 MPa. The tensile strength of the material has been significantly enhanced.
		FDA Certification

|Food Grade PA66 FR30 Application

Food-grade PA66 has excellent heat resistance.Its high heat distortion temperature (HDT)enable it to withstand high-temperature disinfection and sterilization processes in food processing, such as boiling water, steam (for example, cooking, pasteurization), and hot filling

Food-grade PA66 has good resistance to many chemical substances and is suitable for packaging and processing equipment of oily foodsIt can resist acidic or alkaline substances and cleaning agents found in common foods at the same time

PA66 GF30 Kitchenware

| PA66 GF30 Properties

Technical Data
Physical Properties	Value	Unit	Test method
Density	1.53	g/cm³	ASTM D792
Shrinkage MD	0.30 - 0.60	%	ASTM D955
Mechnical Properties	Value	Unit	Test method
tensile strength	120	MPa	ASTM D638
Flexural Strength	210	MPa	ASTM D790
IMPACT	Value	Unit	Test method
Charpy Notched Impact Strength	13	kJ/m²	ISO 179
Charpy Unnotched Impact strength	85	kJ/m²	ISO 179
Thermal Properties	Value	Unit	Test method
HDT 1.8 MPa,unannealed	250	℃	ASTM D648
Electrical Properties	Nominal value	Unit	Test method
Dielectric strength
2 mm	30	kV/mm	ASTM D149
Dielectric constant
1 MHz	3.20		ASTM D150
FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame Class Rating
3.20 mm	V-0		UL94
Injection Conditions	Value	Unit	Test method
Drying temperature	130	℃
Drying time	4.0	hr
Barrel rear temperature	220 to 265	℃
Barrel middle temperature	260 to 270	℃
Barrel front temperature	260 to 270	℃
Nozzle temperature	260 to 270	℃
Mold temperature	60 to 90	℃
Injection pressure	60.0 to 120	MPa