PPS CF10 Pellets Specialized for filaments
PPS CF10 Pellets is 10% carbon fiber reinforced PPS(Polyphenylene sulfide).With easy flow and high purity,Specialized for extrusion PPS CF10 3D printing filaments.
How to verify whether our PPS CF10 is suitable for you?
You can buy small quantity to extrusion to test the pellet quality,and you can get some PPS CF10 printing filament to print.Our PPS CF10 printing filaments is also extruson by this grade.
So you can use some of my printing filaments to test it and see if the printing is smooth and if the nozzle is prone to clogging. This way, the final users can directly check whether it is suitable for them, and then use the granules for large-scale production, significantly reducing the cost and time of trial.
We have 500g, 700g and 1KG of PPS CF10 filaments in stock. You can choose the one according to your actual testing requirements. If you don't need that much, I can provide 10 to 15 meters(or based on your require).
|PPS CF10 Pellets performance
this technical data sheet for reference regarding the material's own properties(Test sample is made by injection) and is not applicable to the performance of the printed components. The components after 3D printing are affected by the inter-layer bonding force, and their mechanical strength may be lower. If you need the performance reference after printing, please refer to PPS CF10 3D printing filaments.
PPS CF10 Physical Properties | Property | Nominal Value | Unit | Test Method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage, MD: 3.2 mm | 0.5 | % | ASTM D955 |
| Water Absorption, balance | 0.040 | % | ASTM D570 |
Mechanical Properties | Property | Nominal Value | Unit | Test Method |
| Tensile Strength (Yield) | 100 | MPa | ASTM D638 |
| Tensile Strain (fracture) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
Impact Properties | Property | Nominal Value | Unit | Test Method |
| Izod Notched Impact Strength | 3.5 | Kj/m 2 | ISO 180/A |
| Izod Unnotched Impact Strength | 20 | Kj/m 2 | ISO 180 |
Thermal Properties | Property | Nominal Value | Unit | Test Method |
| HDT, 1.8 MPa, unannealed | 105 | °C | ASTM D648 |
| Vicat Softening Temperature | 225 | °C | ASTM D1525 2 |
Flame retardant property | Thickness | Nominal Value | Test Method |
| 1.60mm | V-0 | UL94 |
| 3.2mm | V-0 | UL94 |